Applications of NDT Methods on Composite Structures in Aerospace Industry
Ulf Schnars, Rudolf Henrich
Airbus
Hünefeldstraße 1-5
D-28199 Bremen, Germany
Keywords
Non-Destructive Testing, NDT, ultrasonic testing, composite inspection, shearography,
thermography, laser ultrasound
Abstract
This paper reviews present NDT methods used for composite inspection in aircraft industry.
Manual and automatic ultrasonic testing with single element transducers and linear phased
array probes in pulse echo and through transmission mode is applied mainly. But also resonance
methods, shearography, thermography and special methods are used. Laser ultrasound
is a candidate for future contactless automatic inspection.
1. Introduction
Composite materials are used more and more in aircraft production. Main composite types
are Carbon Fibre Reinforced Plastics (CFRP), Glass Fibre Reinforced Plastics (GFRP) and
metal-aluminium laminates (e. g. Glass Fibre Reinforced Aluminium GLAREÓ). Typical parts
made of CFRP are flaps, vertical and horizontal tail planes, center wing boxes, rear pressure
bulkheads, ribs and stringers. For the Airbus A380 GLARE is used even for some shells of
the upper fuselage. The weight percentage of composites in modern civil aircrafts like the
A380 is in the order of 25%. It may be expected that this percentage will further increase for
the next generation of civil aircrafts and that main structure parts like fuselage and wings will
be composed of composites, too.
These composite parts require adequate Non-Destructive Testing (NDT) methods. NDT is
applied in production as well as during maintenance (in-service). Flaws to be detected are
delaminations and debondings, porosity and foreign body inclusion. The most applied NDT
method is ultrasonic testing (manual as well as automatic, in pulse echo and through transmission,
with single element transducers and linear phased array probes). But also resonance
methods, shearography and thermography and special methods are used. This papers
reviews the present NDT methods for composite inspection in aircraft industry and reports
about future demands.
2
2. Manual and Automatic Ultrasonic Testing
Manual ultrasonic testing with single element transducers is still the most applied method for
composite parts with small and medium size. The inspectors are evaluating the A-scans for
flaw detection. Flaw sizes are measured by manual scanning of the probe around the maximum
echo, e. g. using the 6dB method.
In the last years the first linear ultrasonic phased array (PA) inspection systems were applied
for aircraft inspection. With PA’s any desired wavefront can be generated by pure electronic
means. The individual transducers are triggered with a certain delay. The superposition of
individual wavefronts results to a new wavefront with the desired properties. The PA techniques
can be used to tilt and focus a sound beam by electronic means and for electronic
scanning of a sound beam. Another advantage with respect to single element transducers is
the availability of images (B-scan, C-scan, S-scan) instead of only A-scans, which allows
better interpretation of signals inside complex structures. An example of PA inspection of a
bonded stringer is shown in figure 1. The signals of various reflecting surfaces and interfaces
can be clearly identified in the B-scan (right part of the figure).
CFK - stringer
CFK – outer skin (thickn.: 2mm - 8mm)
PHASED ARRAY – Probe / 5MHz
128 elements (Array: 96mm x 10mm)
+ water path
1
128
Wasservorlaufstrecke
Backwall echo outer skin (BE)
Intermediate echo glue line (IE)
Backwall echo stringer (BE)
No backwall echo on stringer web
z.B.: A – scan, element 65
5L128E96-
10
Surface echo outer skin (FSE)
FSE
IE
B
E
Figure 1: Phased Array Inspection of Stringer Skin Bonding
Big CFRP parts are inspected automatically or semi-automatically with multi-channel facilities.
Such machines consist of a portal, which moves the inspection probe over the surface
of the part. An example from an Airbus multi-channel facility working in pulse-echo mode is
shown in figure 2. The probe consists of 96 individual transducers (channels). The maximum
testing area is 13m ´ 7m, with a speed of 100mm/s. The part in the figure is a rear pressure
bulkhead. At Airbus multi-channel facilities are used to inspect vertical and horizontal tail
planes (shells, up to 10 meter long), rear pressure bulkheads, flaps and other long or big
CFRP parts. Evaluation of data is assisted by special software tools.
3
Figure 2: left: Airbus Stade Multi-channel Facility No. 2; right: D-scan
3. Air-Coupled Ultrasound
In ultrasonic testing a coupling medium (usually water) is used to couple the sound field in
the component with minimum losses. Losses due to reflection occur at interfaces, where the
sound impedance changes drastically. This is the case e. g. at the interface between air and
part. This impedance change is much lower between water and part. The coupling medium
reduces therefore the losses.
However, there are components which should have no contact with water or any other coupling
medium. This is the case e. g. for honeycomb components and sandwich parts or parts
with a foam core. For such components the air-coupled method can be applied. This technique
uses a high sound pressure to compensate losses and low frequencies (50kHz to
some 100 kHz). The scheme of air-coupled ultrasonic testing in transmission is shown in
figure 3, an example is shown in figure 4. A double shell structure with foam core inside is
investigated by impact tests. The stringer debonding is clearly visible in the C-scan.
Zeit
Amplitude
Zeit
Amplitude
Transmitter Receiver
Transmitter Receiver
Flaw
Figure 3: Air-Coupled Ultrasonic Testing
4
Figure 4: Air-coupled UT Example: Double Shell Structure (top), C-scan (lower bottom)
5. Porosity Measurement
Prorosity in composites may degrade the stiffness of the structure. Porosity has to be detected
therefore in production. At Airbus Germany the requirement is that at most 2.5% volume
porosity is allowed. An ultrasonic testing method has been developed and qualified to
detect porous areas in CFRP components.
In porous areas often no intermediate echo occurs, because pores may scatter the incident
sound in all directions. The method is therefore based on measurement of backwall echo
reduction due to pores. The backwall echo amplitude decreases, if the sound wave is attenuated
by porosity. It could be shown, that there is a good correlation between backwall
echo reduction and volume porosity determined by micrographic analysis, see figure 5. Such
correlation diagrams are recorded for all different material type and thickness combinations
5
used in production. The similarity of ultrasonic behaviour regarding porosity was shown by
approved statistical tests performed on a large data basis. Because of this similarity, different
material types may be merged. As a result a unique ultrasonic backwall echo reduction
threshold value for classifying porosity as greater than 2.5% by volume has been elaborated.
These threshold values depend on thickness only and are decisive for all epoxy resins reinforced
by carbon fibres in unidirectional built-up, fabric built-up and mixed built-up (based
upon statistical security by an adequate confidence level). Similar threshold values will be
available soon also for GFRP.
0
2
4
6
8
10
12
14
16
18
0 0,5 1 1,5 2 2,5 3
Porosity [% by volume]
BE reduction [dB]
Figure 5: Ultrasonic Backwall Echo Reduction versus Volume Porosity
4. Laser Ultrasonic Testing
Laser ultrasonic testing combines features of optical inspection (contactless, twodimensional)
with those of ultrasonic testing (looking inside the part), see scheme in figure 6.
A pulse laser is directed onto the surface of the component under test. It generates an ultrasonic
wave, propagating in the material. As for conventional ultrasonic testing the signal is
reflected at flaws and interfaces (backwall). The reflected signal is detected optically, e. g.
using a second (long pulse) laser and an interferometer. After filtering the detected signal is
similar to a conventional A-scan. Scanning of the focussed laser pulse over the surface generates
a C-scan.
The main advantage of laser UT is that the sound waves propagate always normally to the
part surface, independently from the incidence angle of the laser light. The method is therefore
predestinated to inspect parts with complex geometry, where conventional multi-channel
systems cannot follow the surface shape and manual testing is not economical. On the other
hand laser UT facilities are (presently) very expensive and complex and have a low scanning
6
speed, because only one channel (laser spout) scans the components. Some development
work is still necessary to make this technique mature for NDT in civil aircraft production.
An example is shown in figure 7. The inspected surface is at the corner. The Laser UT Ascan
is comparable to A-scans of conventional ultrasonic testing. Normally this part is inspected
manually. An automatic inspection by conventional ultrasonic testing with transducers
is difficult due to the complex geometry.
Figure 6: Laser UT
Inspected surface A-scan
Backwall
echo
Surface
echo
C-scan artifical flaws
Figure 7: Laser UT Inspection of a Component with Curved Geometry
7
7. Shearography
20 years ago the NDT community was very enthusiastic concerning the capability of the new
method Holographic Interferometry (HI). Hi is an optical two-dimensional method with very
high sensitivity. With this method even smallest defects could be found. However, after a
short period Hi was discarded for NDT purposes (not for quantitative deformation measurement),
mainly due to two disadvantages. On the one hand the complicated chemical development
process of holographic media was not acceptable for measurements in production
environment (even the thermoplastic film with semi-automatic development could not solve
this problem). Secondly, the price for the high measurement sensitivity was the sensitivity of
the measurement apparatus to vibrations.
The next step in interferometric measurement was Electronic Speckle Pattern Interferometry
(ESPI), which replaced the holographic film by an electronic target, but led the vibration problem
still unsolved. So ESPI was also an intermediate step.
Finally Shearography also solved the vibration problem, because both interfering beams are
guided via the possibly vibrating component. Meanwhile complete shearography systems
with laser, optical head and computer controlled data recording and evaluation are commercially
available.
Airbus applied shearography to several CFRP inspection problems. One example is shown
in figure 8. Flaws due to incorrect repair of the spoiler are clearly visible in the unwrapped
phase map. Shearography is mature for aircraft applications, but it competes with existing
solutions, mainly with ultrasonic testing. A big advantage of shearography is that it is contactless
and delivers directly two-dimensional information. Debondings and delaminations are
easily detectable. On the other hand porosity is difficult to detect, because there is no direct
correlation between the measured surface deformation and the pores inside. Shearography
is therefore a candidate for in-service application, where porosity detection is not required.
Possible applications are detection of stringer debondings or other flaws caused by damage,
e. g. impact damages.
8
Figure 8: Shearography Measurement
8. Conclusions and Outlook
Ultrasonic testing is a standard method for CFRP inspection. Manual testing with single element
transducers is applied for small parts, big parts are tested with multi-channel facilities.
The phased array technology (with linear arrays) is entering more and more in production
and in-service. Laser ultrasonic testing still in the laboratory phase, but has potential for inspection
of parts with small and medium size and complex geometry. Shearography is
meanwhile an established method, but until now only a few real applications in production or
in-service exist.
Future challenges in NDT for CFRP are driven by a potentially higher percentage of composite
in aircraft structure. This requires more in-line inspection tools, i. e. an integration of NDT
in the manufacturing process chain. Today “parts meets the NDT system”, in future this
should be vice versa - “the NDT system should meet the part”. In some cases manufacturing
processes could be supervised by pure on-line system, replacing classical NDT.
Furthermore production needs NDT methods, which are sensitive only to defects. It is not
economic for an inspector to spend 99% of the evaluation time to look on faultless areas. It is
much better to have a system, which guides him directly to suspicious areas. A further step is
then to develop intelligent defect identification tools, which can decide between genuine defects
and spurious indications.
For preparation of NDT procedures it is often necessary to perform extensive laboratory investigations,
in which all potential combinations of part geometry, flaw size and position,
probe configurations etc. are tested. In future NDT modeling tools may help to reduce such
investigations by replacing them partially by numerical simulations.

使用道具 举报

Rank: 1

3#
发表于 2011-5-28 09:04:14 |只看该作者
值得拥有~好好学习

使用道具 举报

您需要登录后才可以回帖 登录 | 注册


Archiver|航空论坛 ( 渝ICP备10008336号 )

GMT+8, 2024-11-21 21:27 , Processed in 0.084005 second(s), 12 queries .

Powered by Discuz! X2

© 2001-2011 MinHang.CC.

回顶部